Template electrosyntesis of CeO2 nanotubes
2007
Nanotube arrays of CeO2 were produced in a single step by potentiostatic electrochemical deposition from a non-aqueous electrolyte, using anodic alumina membrane templates. The CeO2 nanotubes showed a polycrystalline structure, and they were assembled in the membrane nanochannels. The nanotubes had somewhat uniform diameters, with an average external value of about 210 nm, and a maximum length of about 60 µm; the latter parameter was controlled by the electrodeposition time. Each single nanotube was found to consist of crystalline grains having a size of about 3 nm. Raman analysis shows that these CeO2 nanotubes are suitable for catalytic applications.
Crystalline-Size Dependence of Dual Emission Peak on Hybrid Organic Lead-Iodide Perovskite Films at Low Temperatures
2018
In this work, we have investigated the crystalline-size dependence of optical absorption and photoluminescence emission of CH3NH3PbI3 films, which is necessary to identify the potential practical applications of the gadgets based on perovskite films. This study was carried out at low temperatures to minimize the extra complexity induced by thermal effects. The purpose was to clarify the origin of the dual emission peak previously reported in the literature. We found that the grain size is responsible for the appearance or disappearance of this dual emission on CH3NH3PbI3 at low temperatures, whereas we have inferred that the thickness of the perovskite layer is a much more important factor …